Hartlot auf Nickelbasis

The nickel-based brazing alloy BrazeLet BNi1 provides high strength joints with excellent oxidation resistance suitable for brazing stainless steels and nickel-based superalloys. It is suitable for brazing in vacuum or protective atmospheres (dry hydrogen or argon). Joint properties can be further improved by employing a diffusion hold after brazing. The brazing alloy is typically used for joining parts subjected to high stresses and temperatures such as turbine components.

The nickel-based brazing alloy BrazeLet BNi1A provides high strength joints with excellent oxidation resistance suitable for brazing stainless steels and nickel-based superalloys. It is suitable for brazing in vacuum or protective atmospheres (dry hydrogen or argon). The alloy is similar to BrazeLet BNi1, but has low carbon content. Joint properties can be further improved by employing a diffusion hold after brazing. The brazing alloy is typically used for joining parts subjected to high stresses and temperatures such as turbine components and diamond tools.

Die Hartlöt-Legierung auf Nickelbasis BrazeLet^® BNi2 bietet hohe Festigkeit beim Löten von Edelstahl im Vakuum oder in Schutzatmosphäre. Die Hartlöt-Legierung wird typischerweise zum Löten von Wärmetauschern verwendet, die keine hohe Korrosionsbeständigkeit erfordern (z. B. AGR-Kühler für Fahrzeuge und Trinkwasseranwendungen im Haushalt oder in der Industrie).

BrazeLet BNi2 enthält Bor zur Reduzierung des Schmelzpunktes und kann daher bei relativ niedrigen Temperaturen eingesetzt werden.

Zusammensetzung

ISO 3677, B-Ni82CrSiBFe-970/1000
ISO 17672, Ni 620
ANSI/AWS A5.8, BNi-2
UNS N99620

Schmelzbereich

970 - 1000 °C

Min. Löttemperatur

1050°C

The nickel-based brazing alloy BrazeLet BNi3 provides high strength joints when brazing in vacuum or protective atmospheres (hydrogen or argon). As it is Cr-free it is less sensitive to marginal furnace atmospheres. The brazing alloy is typically used for brazing nickel-based superalloys and stainless steel components where high elevated temperature strength is important, such as turbine vanes or honeycomb seals.The alloy also has good oxidation resistance. Joint properties can be further improved by employing a diffusion hold after brazing.

The nickel-based brazing alloy BrazeLet BNi4 provides high strength joints when brazing in vacuum or protective atmospheres (hydrogen or argon). As it is Cr-free it is less sensitive to marginal furnace atmospheres. The brazing alloy is typically used for brazing nickel-based superalloys and stainless steel components where high elevated temperature strength is important, such as turbine vanes and honeycomb seals. The alloy also has good oxidation resistance. Joint properties can be further improved by employing a diffusion hold after brazing.  Compared to the similar BrazeLet BNi3, BrazeLet BNi4 has better gap filling ability and provides more ductile joints.

BrazeLet^® BNi5 ist eine Hartlöt-Legierung auf Nickelbasis mit guten Benetzungseigenschaften auf Edelstahl beim Löten im Vakuum oder in einer Schutzatmosphäre. 

Der hohe Gehalt an legiertem Chrom führt zu einer guten Heißgas- und Säurekorrosionsbeständigkeit. Dank hohem Schmelzbereich ist BrazeLet BNi5 für Anwendungen mit sehr hohen Temperaturen, z. B. AGR-Kühler für Lkw und Metall-Katalysatoren für Pkw, geeignet.

Zusammensetzung

ISO 3677, B-Ni71CrSi-1080/1135
ISO 17672, Ni 650
ANSI/AWS A5.8, BNi-5
UNS N99650

Schmelzbereich

1080-1135°C

Min. Löttemperatur

1150 °C

The nickel-based brazing alloy BrazeLet BNi6 is a free-flowing material suitable for brazing low-carbon steels and stainless steels. It is suitable for brazing in vacuum or protective atmospheres (dry hydrogen, nitrogen/hydrogen mixtures or argon) and is also suitable for marginal furnace atmospheres. It allows brazing at lower temperatures than any of the other nickel-based brazing alloys. It is particularly suitable for brazing deep narrow joints as it maintains the excellent flowability with limited P diffusion into most base materials. It is recommended that gaps do not exceed 30 µm as wider gaps risk the formation of a crack-sensitive brittle centre line.

BrazeLet^® BNi7 ist eine Hartlot-Legierung auf Nickelbasis mit hoher Festigkeit beim Löten von Edelstahl im Vakuum oder in einer Schutzatmosphäre. Typische Anwendungen für diese Hartlot-Legierung sind Wärmetauscher, die keine hohe Korrosionsbeständigkeit erfordern, z. B. AGR-Kühler für Fahrzeuge und Trinkwasseranwendungen im Haushalt oder in der Industrie.

BrazeLet BNi7 enthält Phosphor zur Reduzierung des Schmelzpunktes und kann daher bei relativ niedrigen Temperaturen eingesetzt werden.

Zusammensetzung

ISO 3677, B-Ni76CrP-890
ISO 17672, Ni 710
ANSI/AWS A5.8, BNi-7
UNS N99710

Schmelztemperatur

890°C

Min. Löttemperatur

980°C

Höganäs’ unique and patented nickel-based brazing alloy BrazeLet Ni623 is a high temperature brazing alloy suitable to use where both base material and the brazed joints require superior corrosion resistance. The alloy is developed and particularly suitable for brazing high-alloyed austenitic and super-austenitic stainless steels which require special heat treatments and rapid cooling from temperatures around 1100 °C to avoid precipitation of deleterious intermetallic phases.