Filtration
Stainless steel powders
Höganäs' filtration media
The production method for this special material is based on high-pressure water atomisation. A liquid metal stream is shattered by water jets into small particles. These grains have an extremely irregular shape.
The porosity volume and particle surface area are dictated by the size and shape of the powder particles. Larger grains tend to give a higher porosity, but a lower active surface area. Finer particles give a higher active surface area, but a somewhat lower porosity volume. The high active surface area ensures good cleaning during filtration.
The filtration particles are made of stainless steel alloys specially developed for hot polymer filtration. The chemical composition is important for the particles’ strength and corrosion resistance.
The alloys used should be strong enough to minimize collapse during filtration and offer stable pressure during the filtration cycle. As the particles are not brittle, they do not crack up during filtration. Consequently there is no risk of the nozzles clogging.
Contact sales & technical support
Contact your sales representative for more information and requests.
Contact us
Kontaktformulär
Kontaktpersoner
Technical area:
Filtration
Välj land *
Typ av kontakt *
Sälj
Sälj
Teknisk support
Förnamn *
Efternamn *
Företag *
Arbetsområde *
VD/ägare
Inköpare
Konstruktör
Affärsutvecklare
Maskinoperatör
Annat
E-post *
Telefon arbete *
Ditt meddelande *
Personuppgiftspolicy
Jag samtycker till att Höganäs får hantera mina personuppgifter för att kontakta mig. Mina kontaktuppgifter kan också användas i marknadsföringssyfte, såsom nyhetsbrev och annan relevant information. Uppgifterna kan komma att delas med våra leverantörer. Med mitt samtycke bekräftar jag även att jag är över 16 år gammal.
Mer information om hur vi hanterar personuppgifter anges i vår personuppgiftspolicy.
Du måste godkänna villkoren för tjänsten för att fortsätta.
Nickel based
P-271
| Fe (%) | Ni (%) | Cr (%) | Mn (%) | Si (%) | Mo (%) | C (%) |
| 7.0-10.0 | Bla | 14.0-17.0 | - | 2.0-2.5 | - | Max 0.03 |
Applications
High oxidation resistance, ideal for spinning of nylon yarn
Oxidation resistance
5+
Stainless steel based
DP-1
| Fe (%) | Ni (%) | Cr (%) | Mn (%) | Si (%) | Mo (%) | C (%) |
| Bla | Max 0.9 | 33.0-37.0 | Max 0.5 | 2.0-4.0 | Max 0.3 | Max 0.04 |
Applications
High pressure filtration, magnetic
Oxidation resistance
4+
P-270
| Fe (%) | Ni (%) | Cr (%) | Mn (%) | Si (%) | Mo (%) | C (%) |
| Bla | 11.0-13.0 | 18.0-22.0 | 0.4-.07 | 2.5-3.5 | 1.0-3.0 | Max 0.02 |
Applications
Standard media for polyester yarn
Oxidation resistance
3+
316L
| Fe (%) | Ni (%) | Cr (%) | Mn (%) | Si (%) | Mo (%) | C (%) |
| Bla | 12.0-14.0 | 16.0-18.0 | Max 0.2 | 0.5-1.0 | 2.0-3.0 | Max 0.03 |
Applications
Ordinary Stainless steel
Oxidation resistance
2+
Typical physical properties
| Size micron | Size mesh | Apparent density g/cm3 |
Tap density g/cm3 |
Porosity % |
| 45-90 | 170/325 | 2.6 | 3.5 | 55 |
| 90-125 | 120/170 | 2.4 | 3.1 | 58 |
| 125-180 | 120/80 | 2.2 | 3.0 | 61 |
| 180-250 | 60/80 | 2.0 | 2.8 | 54 |
| 250-355 | 45/60 | 1.8 | 2.6 | 55 |
| 355-500 | 35/45 | 1.7 | 2.2 | 71 |
| 500-850 | 20/35 | 1.7 | 2.1 | 73 |
| 850-2000 | 10/20 | 1.5 | 1.9 | 75 |
| Alternative cuts | ||||
| 150-300 | 50/100 | 1.9 | 2.1 | 73 |
| 180-425 | 40/80 | 1.8 | 2.0 | 74 |
| 250-600 | 30/60 | 1.7 | 1.9 | 74 |
| 300-710 | 25/35 | 1.7 | 1.85 | 75 |
| 710-2000 | 10/25 | 1.5 | 1.8 | 76 |
Metallpulver bidrar till hållbar utveckling
Metallpulverteknik erbjuder obegränsade möjligheter. Våra kunder kan inte bara reducera material- och energiförbrukning, utan också utnyttja nya och bättre lösningar som gör slutprodukten effektivare och billigare.
Vi tror att den inbyggda kraften i metallpulver kan användas i betydligt större utsträckning än vad som är fallet idag. Vi är också övertygade om att metallpulver kan bidra till en hållbar miljö. Med metallpulverlösningar kan vi bidra till att lösa många problem i samhället, till exempel resursbrist och behov av förnybar energi.