BrazeLet® F300
BrazeLet® F300 is a unique stainless iron-chromium-based brazing filler metal for applications operating in extreme environments. Its unique chemical composition delivers similar corrosion resistance and joint strength properties to high-performing nickel-based filler metals. However, it is a more cost-effective alternative thanks to the use of less costly metals.
BrazeLet F300 has excellent wetting properties, low brazing temperature and creates a uniform joint with high strength and high corrosion- and oxidation resistance, making it suitable for heat exchanger applications in industry and the automotive sector.
The first choice for the increasing demand of copper-free brazing, e.g. for drinking water applications and oil coolers.
Benefits
- Cost-efficient
- Wide gap flexibility
- Corrosion resistant
- High strength
Composition
ISO 3677, B-Fe39CrNiCuPSi-1000/1070
Impurities according ISO 17672
Impurities according ANSI/AWS A5.8
Melting temperature
1000-1070 °C
Min. brazing temperature
1100 °C
Ladda ner
Läs mer
Contact us
Sales & technical support
Personuppgiftspolicy
Jag godkänner att Höganäs hanterar mina personuppgifter för att kontakta mig. Min kontaktinformation kan även komma att användas för marknadsföringsändamål, som nyhetsbrev och annan relevant information. Uppgifterna kommer inte att delas med någon tredje part. I och med detta samtycke bekräftar jag även att jag är över 16 år.
Mer information om hur vi hanterar personuppgifter anges i vår personuppgiftspolicy.